BSM Aconia Master 3D Multilayer Zirconia

Multilayer Zirconia Designed for Strength, Esthetics, and Efficient Production

BSM Aconia Master 3D is a multilayer zirconia designed for dental laboratories looking for a combination of high strength and natural-looking esthetics in monolithic restorations. Its multilayer structure provides gradual shade transitions throughout the disc, creating greater depth and a more lifelike appearance after sintering.

With flexural strength ranging from 800–1200 MPa, Aconia Master 3D is suitable for a broad range of restorations, from individual crowns to demanding full-arch implant-supported cases. The material is engineered to maintain dimensional stability and predictable performance throughout the sintering process.

Key Benefits

Natural Multilayer Esthetics
The integrated multilayer shade gradient provides a smooth transition between cervical, dentin, and incisal areas, helping create natural-looking restorations with minimal additional characterization.

High Strength for Demanding Cases
With flexural strength of 800–1200 MPa and fracture toughness exceeding 5.2 MPa·m½, Aconia Master 3D provides the strength needed for posterior restorations, bridges, and other high-load applications.

Flexible Sintering Range
Aconia Master 3D can be sintered within a temperature range of 1520°C–1560°C, providing flexibility when integrating the material into different laboratory workflows.

Efficient Production
The material supports high-speed sintering when used with the appropriate BSM sintering program, helping laboratories reduce turnaround times without sacrificing the consistency of the finished restoration.

Consistent Dimensional Stability
Aconia Master 3D is engineered for low deformation during sintering, supporting accurate fits and helping reduce the need for remakes and adjustments.

Material Specifications

• Flexural Strength: 800–1200 MPa
• Translucency: 43–51%
• Vickers Hardness: 1250–1350 HV10
• Sintered Density: >6.02 g/cm³
• Fracture Toughness: >5.2 MPa·m½
• Disc Diameter: 98.5 mm
• Available Thicknesses: 12, 14, 16, 18, 20, 22, 25 mm
• Available Shades: A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4, OM1, OM2, OM3

Recommended Applications

• Monolithic crowns
• Multiple-unit bridges
• Posterior restorations
• Full-arch implant-supported restorations
• High-strength zirconia restorations

Aconia Master 3D combines multilayer esthetics with high mechanical strength, giving dental laboratories a versatile zirconia option for everyday crowns as well as more demanding restorative cases.